Raw Material Selection
The manufacturing process of buttweld fittings begins with the careful selection of raw materials.
A high level of quality standards is maintained by SHEETAL INDUSTRIES Manufacturers through stringent quality checks at every stage of production. In order to ensure that our products are of the highest quality, we only use premium raw materials. A high level of quality standards is maintained by SHEETAL INDUSTRIES Manufacturers through stringent quality checks at every stage of production. In order to ensure that our products are of the highest quality, we only use premium raw materials. A high level of quality standards is maintained by SHEETAL INDUSTRIES Manufacturers through stringent quality checks at every stage of production.
Table Of Content
A high level of quality standards is maintained by SHEETAL INDUSTRIES Manufacturers through stringent quality checks at every stage of production. In order to ensure that our products are of the highest quality, we only use premium raw materials. A high level of quality standards is maintained by SHEETAL INDUSTRIES Manufacturers through stringent quality checks at every stage of production. In order to ensure that our products are of the highest quality, we only use premium raw materials. A high level of quality standards is maintained by SHEETAL INDUSTRIES Manufacturers through stringent quality checks at every stage of production.
A high level of quality standards is maintained by SHEETAL INDUSTRIES Manufacturers through stringent quality checks at every stage of production. In order to ensure that our products are of the highest quality, we only use premium raw materials. A high level of quality standards is maintained by SHEETAL INDUSTRIES Manufacturers through stringent quality checks at every stage of production. In order to ensure that our products are of the highest quality, we only use premium raw materials. A high level of quality standards is maintained by SHEETAL INDUSTRIES Manufacturers through stringent quality checks at every stage of production.
Specifications | ASTM A403 / ASME SA403 |
Size | Seamless Butt Weld Fittings: 1/2" - 10" Welded Butt Weld Fittings: 1/2" - 48" |
Thickness | SCH10, SCH20, SCH30, STD SCH40, SCH60, XS, SCH 80, SCH 100, SCH 120, SCH 140, SCH 160, XXS available with NACE MR 01-75 |
Type | DN15-DN1200 |
Dimensions | ASME/ANSI B16.9, ASME B16.28, MSS-SP-43, BS4504, BS4504, BS1560, BS10 |
Bending Radius | R=1D, 2D, 3D, 5D, 6D, 8D, 10D or Custom MSS Sp-43 Stainless Steel Pipe Fitting |
Size Range | ½" NB to 24" NB in Sch 10s, 40s, 80s, 160s, XXS. (DN6~DN100) ASTM A403 Stainless Steel Buttweld Fitting |
Elbows | Angle : 22.5 deg, 30deg, 45 deg, 90 deg, 180 deg, 1.0D, 1.5D, 2.0D, 2.5D,
3D, 4D, 5D, 6D, 7D-40D . Standard: ASME B16.9, ASME B16.28, ASME B16.25, MSS SP-75 DIN2605 JISB2311 JISB2312 JISB2313, BS, GB, ISO |
Connection | Welding |
Manufacturing process | Forge, Cast, Push, Press, etc. |
Key markets and industries |
Bitumen upgraders. Heavy oil refineries. Petrochemicals and acids. Nuclear power (mostly seamless). |
Test Certificates | EN 10204/3.1B Raw Materials Certificate 100% Radiography Test Report Third Party Inspection Report, etc |
Specialized manufacturer of | 90º Elbows, 45º Elbows, Tees, Crosses, Reducers, Pipe Cap, Stub End, Pipe Bend |
We provide Material Test Certificates (MTC) as per EN 10204 3.1 and EN 10204 3.2, Test Certificates certifying NACE MR0103, NACE MR0175 |
USA | France | North America | Germany | Germany | Italy | Japan | Russia | Spain | Sweden | UK | European Union |
AISI | AFNOR | UNS | DIN 17006 | W.N. 17007 | UNI | JIS | GOST | UNE | SIS | BSI | EURONORM |
304 | Z 6 CN 18-09 | S30400 | X 5 CrNi 18 10 X 5 CrNi 18 12 | 1.4301 | X 5 CrNi 1810 | SUS 304 | 08KH18N10 06KH18N11 | X 6 CrNi 19-10 | 23 32 | 304S15 304S16 | X 6 CrNi 18 10 |
304L | Z 2 CN 18-10 | S30403 | X 2 CrNi 18 11 | 1.4306 | X 2 CrNi 1911 | SUS 304L | 03KH18N11 | X 2 CrNi 19-10 | 23 52 | 304S11 | X 3 CrNi 18 10 |
304H | - | S30409 | - | 1.4948 | X 8 CrNi 1910 | SUS F 304H | - | X 6 CrNi 19-10 | - | - | - |
Grade | C | N | Si | P | S | Cr | Mn | Ni | Fe |
304 | 0.08 max | 0.10 max | 0.75 max | 0.045 max | 0.030 max | 18.0 - 20.0 | 2.0 max | 8.0 - 10.5 | Remainder |
304L | 0.03 max | 0.10 max | 0.75 max | 0.045 max | 0.030 max | 18.0 - 20.0 | 2.0 max | 8.0 - 12.0 | Remainder |
304H | 0.04 - 0.10 | 0.10 max | 0.75 max | 0.045 max | 0.030 max | 18.0 - 20.0 | 2.0 max | 8.0 - 10.5 | Remainder |
Grade | Tensile Strength (ksi) | 0.2% Yield Strength (ksi) | Elongation% in 2 inches |
304 | 75 | 30 | 40 |
304L | 70 | 25 | 40 |
304H | 75 | 30 | 40 |
Properties | Units | Temperature in °C |
Density | 8.03 g/cm³ | Room |
Specific Heat | 0.12 Kcal/kg.C | 22° |
Melting Range | 1399 - 1454 °C | - |
Modulus of Elasticity | 193 KN/mm² | 22° |
Electrical Resistivity | 72 µΩ.cm | Room |
Coefficient of Expansion | 16.9 µm/m °C | 20 - 100° |
Thermal Conductivity | 16.2 W/m -°K | 20° |